- Coupling Agents Treatment of Electro-conductive White Powders Coated with In2O3-Sn Film.
- In2O3-Snケイ ハクショク ドウデン フン ノ カップリングザイ ショリ
この論文をさがす
抄録
In a previous paper the authors reported a novel wet preparation method for electro-conductive white powders homogeneously coated with In2O3-Sn film. Further experiments were performed to obtain insight into aging treatment of the suspension after hydrolysis reaction of the ITO compound, and into coupling agent treatment to stabilize the electro-conductivity of the resulting powders. The electro-conductivity of the final product was greatly improved by aging a suspension of fine powders coated with mixed ITO composition hydroxides for 60 minutes at pH 6.5±0.5 and 343K. Generally, the electro-conductivity of ITO-coated powders deteriorates owing to the influence of atmospheric oxygen. Coupling agent treatment of ITO-coated powders was found to be very effective in averting this effect. The applicability of various coupling agents, both silane type and titanate type, were examined. A coupling agent is an insulator by nature, so the use of excess amounts must be avoided. However, a suitable amount of coupling agent treatment exhibited remarkable effectiveness in improving the electro-conductivity of ITO-coated powders. A silane type coupling agent with a mercapto group was particularly effective. The decay of electro-conductivity over time caused by oxygen can be almost completely averted by use of coupling agent.
収録刊行物
-
- 表面技術
-
表面技術 47 (5), 433-437, 1996
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204113816960
-
- NII論文ID
- 10002256354
-
- NII書誌ID
- AN1005202X
-
- COI
- 1:CAS:528:DyaK28Xjt1ygtbs%3D
-
- ISSN
- 18843409
- 09151869
- http://id.crossref.org/issn/09151869
-
- NDL書誌ID
- 3960067
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可