- Effect of the Heat Treatments to Microstructures of Low Pressure Plasma Sprayed CoNiCrAlYTa Coating.
- ゲンアツ プラズマ ヨウシャシタ CoNiCrAlYTa ヒマク ノ ビサイ
この論文をさがす
抄録
In this study, transmission electron microscopy (TEM) was used to characterize the microstructures of as-sprayed, solution-treated, aged CoNiCrAlYTa coatings. The micro-vickers hardness test was used to estimate age hardening of the coatings. The hardness of as-sprayed coatings was about 590Hv. Hardness was decreased to about 560Hv in solution treatment at 1373K for 4 hours. It was increased, however, by aging at 1073K and 1173K after solution treatment.<br>TEM observation showed that the average grain size was about 0.5μm. The γ and β-phases coexisted in as-sprayed coatings. Solution treatment at 1373K coarsened the grain size to about 1.5μm. Wedge-shaped β precipitates in the γ-phase were produced by aging. Needle-shaped α-Co and massive σ precipitates in β phase were clearly produced by aging. These precipitations are therefore thought to contribute to age hardening.
収録刊行物
-
- 表面技術
-
表面技術 47 (9), 784-789, 1996
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679091464320
-
- NII論文ID
- 10002257169
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 4028868
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可