プラズマを利用したフッ素ゴムとアルミニウムとの接着 Adhesion of Fluorine-containing Rubber to Aluminum Subjected to Plasma Treatments

この論文にアクセスする

この論文をさがす

著者

抄録

The adhesion strength of fluorine-containing rubber (a copolymer of CF<sub>2</sub>=CH<sub>2</sub> and CF<sub>2</sub>=CF-CF<sub>3</sub>) to plasma treated aluminum was studied using X-ray photoelectron spectroscopy data and the water contact angle. Plasma treatments were as follows. (a) argon plasma treatment of aluminum at elevated temperatures in the presence of polytetrafluoroethylene (PTFE), sputtering PTFE onto the metal surface and (b) argon plasma treatments in the absence or in the presence of PTFE of plasma polymerized film (PPF) of cyclohexane previously formed on the aluminum surface. Adhesion was conducted by inserting rubber between two treated aluminum samples and adding compressive stress at high temperature. Adhesive strength was measured using Instron test equipment. Adhesive strength using treatment (a) was much greater than without treatment and slowly increased with increasing temperature, being due to the removal of carbon contaminants and the introduction of CF<sub>2</sub> groups on the surface. Adhesive strength using treatment (b) increased several times compared to that without plasma treatments. The PPF surface after treatment (b) exhibited a hydrophihc nature, thought to play a significant role in adhesion.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan  

    表面技術 = The Journal of the Surface Finishing Society of Japan 47(11), 927-933, 1996-11 

    The Surface Finishing Society of Japan

参考文献:  12件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002257473
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4087647
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ