バリヤー型アルミニウム陽極酸化皮膜へのEuイオン注入とエレクトロルミネセンス Eu Ion Implantation into a Anodic Oxide Barrier Film on Aluminum and its Electroluminescence

この論文にアクセスする

この論文をさがす

著者

抄録

For the development of electroluminescence devices made from anodic oxide films on aluminum, Eu ions were implanted into a barrier film, and red electroluminescence from Eu<sup>3+</sup> was observed during film reanodization.<br>Red electroluminescence from specimens without surface pretreatment occurred at about 100V and its intensity raised with increasing of voltage. It also continued for several minutes with a weak current density of 0.03mA·cm<sup>-2</sup> at a constant voltage of 350V.<br>Luminescence intensity was influenced by surface conditions, so electroluminescence from specimens without surface pretreatment was 7 times stronger than with electropolishing. Electroluminescence intensity was thus considered to be influenced by flaws in the film.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan  

    表面技術 = The Journal of the Surface Finishing Society of Japan 47(12), 1070-1074, 1996-12-01 

    The Surface Finishing Society of Japan

参考文献:  10件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002257976
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4106793
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ