反応性イオンプレーティング法による金・窒化アルミニウム複合薄膜の形成 Au・AIN Composite Films Formed by Reaction Ion Plating Method

この論文にアクセスする

この論文をさがす

著者

抄録

Deposition of black-colored films whose mayor component is gold using the RF ion plating method was investigated, and the results were evaluated. Au-Al alloys were used as the evaporation source material. AlN was first produced by the reactive ion plating method using nitrogen gas as the reactive gas and the evaporation conditions of Au and AlN composite black films were then studied. Black Au-AlN composite films with high corrosion resistance were obtained on the substrate under conditions of an RF power of 150W, a bias voltage of 500V and an evaporation rate of 36nm/min. To examine the potential for commercial use, the same lustrous black composite films were produced on post earrings (K18 and K14) under the same conditions as mentioned above. These results open up new possibilities for design of ornaments and production of value-added goods.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan  

    表面技術 = The Journal of the Surface Finishing Society of Japan 48(1), 36-41, 1997-01-01 

    The Surface Finishing Society of Japan

参考文献:  11件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002258107
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4118794
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ