The Effects of Ar Pressure on Corrosion and Structural Property of r.f. Magnetron Sputtered AlN Thin Film Deposited on Al-Mg Alloy.

DOI Web Site 1 Citations 19 References

Bibliographic Information

Other Title
  • スパッタ法でＡｌ‐Ｍｇ合金基板上に成膜したＡｌＮ薄膜の防食特性および皮膜構造に与える成膜時のＡｒガス圧の影響
  • スパッタホウ デ Al-Mg ゴウキン キバンジョウ ニ セイマクシタ AlN

Search this article

Abstract

A series of AlN thin films was synthesized on Al-25mass%Mg substrate under different Ar pressures from 007 to 1.3Pa using rf magnetron sputtering. The effects of Ar pressure on the corrosion protection in a 5mass%NaCl solution and structural properties were studied. As Ar pressure was increased above 027Pa, the corrosion resistance of the AlN-coated Al-Mg alloy was significantly improved. Residual film stress was compressive under low Ar pressures, which decreased as Ar pressure increased and turned tensile at high Ar pressures. An obvious correlation was observed between the corrosion protection property and residual stress. A coating with low residual stress was superior in corrosion protection to a coating with high compressive residual stress. The change of the corrosion protection property is discussed in connection with the residual stress of the sputtered film. The origin of the residual stress in the AlN coating is also discussed from the viewpoint of the energy change in sputtered particles.

Journal

Citations (1)*help

See more

References(19)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top