In order to examine the corrosion process of Zn-Ni alloy electroplated steel in a solution containing chlorine ions (3%NaCl aqueous solution), the time dependence of the corrosion potential was measured during an immersion test and the corrosion products were analyzed by XPS. The corrosion potential shifted to a noble potential in a complex manner as corrosion proceeded. The shift of the corrosion potential was characterized by the following corrosion process. At the beginning of corrosion, selective dissolution of Zn occured, and Zn oxide or hydroxide formed as a corrosion product on the surface of the Zn-Ni alloy plating. In the early stages of corrosion, the thickness of the corrosion product layer increased. As corrosion progressed, ZnCl2·4Zn(OH)2 formed outside the Zn oxide (hydroxide) layer. Therefore, the surface of the Zn-Ni alloy electroplated steel took on a layered structure of ZnCl2·4Zn(OH)2/Zn oxide or hydroxide/Zn oxide or hydroxide+metallic Ni/steel substrate. Dissolution of iron from the underlying steel occurs by passing through these corrosion products layers.
収録刊行物
-
- 表面技術
-
表面技術 48 (2), 206-212, 1997
一般社団法人 表面技術協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204115545984
-
- NII論文ID
- 10002258398
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 4139979
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可