The Properties of the Bright Silver Deposit from Cyanide-Free Bath.
-
- MASAKI Seishi
- Daiwa Fine Chemicals Co., Ltd.
-
- INOUE Hiroyuki
- College of Eng., Osaka Pref. Univ.
-
- YAMAKAWA Koji
- College of Eng., Osaka Pref. Univ.
Bibliographic Information
- Other Title
-
- 非シアン浴から得られた光沢銀電析物の皮膜特性
- ヒ シアンヨク カラ エラレタ コウタク ギン デンセキブツ ノ ヒマク トク
Search this article
Abstract
The properties of electrodeposited silver films from succinimide baths were iuvestigated using a bath composed of 0.45mol/L of CH3SO3Ag and 1.5mol/L of succinimide. The silver film grain size was similar to that from a bright cyanide bath. The optimum conditions for bright silver plating were a pH of 10, a bath temperature of 25°C, and a current density of 2A/dm2.<br>The plating bath throwing power was 40-42% and increased with the pH. The solderability of these silver deposits was better than those from a bright cyanide bath and the film electric contact resistance was less than 2mΩ at a load of 5g. The deposited silver hardness was Hv (125-130) and became Hv (86-90) after backing at 200°C for 1h.
Journal
-
- Journal of The Surface Finishing Society of Japan
-
Journal of The Surface Finishing Society of Japan 48 (6), 643-646, 1997
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679092600960
-
- NII Article ID
- 10002259278
-
- NII Book ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL BIB ID
- 4237643
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed