Ａｌ単結晶表面上へのジンケート処理と無電解Ｎｉ‐Ｐめっき

• 中田 毅

  芝浦工業大学 工学部

• 和田 一郎

  芝浦工業大学 大学院

• 今井 八郎

  芝浦工業大学 工学部

• 池島 賢司

  芝浦工業大学 大学院 現 メルテックス (株)

• 井上 晃一郎

  芝浦工業大学 大学院

• 渡辺 徹

  東京都立大学 工学部

書誌事項

タイトル別名

• Zincate Treatment and Electroless Ni-P Plating on Al Single-Crystal Surface.
• Al タンケッショウ ヒョウメンジョウ エ ノ ジンケート ショリ ト ムデン

抄録

Zincate treatment and electroless Ni-P plating were conducted on the {100}, {110} and {111} surfaces of Al single crystal produced using the Bridgman method. The deposition morphology of Zn particles and Ni-P film were studied through SEM observation and different crystallographic orientation. Once deposition of Zn reached a certain level, it increased only negligibly there after. Zn particles deposited after the second zincate treatment were refined and made homogeneous by dissolution in immersion in HNO₃ solution after the first zincate treatment. It was recognized that convex objects were observed on the surface after Zn particle dissolution, and also deposited on the top of convex objects by the second zincate treatment. The differences in convex objects were recognized on the crystal surface of the Al single crystal. Observation of the plating layer surface morphology showed the {111} surface to have the most homogeneous, smoothest surface.

収録刊行物

• 表面技術

  表面技術 48 (8), 820-825, 1997

  一般社団法人 表面技術協会

キーワード

• Single Crystal
• Zincate Treatment
• Electroless Ni-P Plating
• Crystallographic Orientation
• Hard Disc

詳細情報

• CRID: 1390001204116033792
• NII論文ID: 10002259623
• NII書誌ID: AN1005202X
• DOI: 10.4139/sfj.48.820
• ISSN: 18843409
• ISSN: 09151869
• NDL書誌ID: 4275775
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4275775
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可