アルカリ性白金-すず合金浴からの析出物の特性 Characteristic of the Deposits from Alkaline Platinum-Tin Alloy Plating Bath

この論文にアクセスする

この論文をさがす

著者

    • 鎗田 聡明 YARITA Somei
    • 日本エレクトロプレイティング・エンジニヤース(株)R&Dセクション Electroplating Engineers of Japan Ltd.

抄録

Platinum-tin alloy plating in a platinum plating solution in the presence of potassium hexahydroxoplatinate and potassium stannate added was studied. Up to 100g/L tin was added to the bath, which contained 10g/L of platinum and its effect on deposit efficiency and alloy composition was analyzed. Based on this, the current efficiency was determined and found to decrease from 90% to 30% with the addition of tin from 5g/L to 10g/L to 15g/L. When more tin was added, current efficiency became about 40%. The codeposition of tin was about 30wt%. Deposits containing 15 to 25wt% of tin were observed to have in excess of 600Hv Vickers hardness. X-ray diffraction imaging determined that, with tin codeposition, platinum deposits were no longer oriented to (200) and the diffraction peak range were broadened.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan

    表面技術 = The Journal of the Surface Finishing Society of Japan 48(11), 1105-1108, 1997-11-01

    The Surface Finishing Society of Japan

参考文献:  21件中 1-21件 を表示

  • <no title>

    BAUMGARTNER M. E.

    Platinum Metals Rev. 32, 4,188, 1988

    被引用文献1件

  • <no title>

    田中清一郎監修

    貴金属の科学応用編 234, 1985

    被引用文献1件

  • <no title>

    SKINNER P. E.

    Platinum Metals Rev. 33, (3), 105, 1989

    被引用文献4件

  • <no title>

    INDIRA K. S.

    Metal Finishing 67, (5), 44, 1969

    被引用文献4件

  • <no title>

    REID F. H.

    Trans. Inst. Metal Finish. 48, 115, 1970

    被引用文献5件

  • <no title>

    鎗田聡明

    表面技術 48(6), 1997

    被引用文献1件

  • <no title>

    SIMON Franz

    Plating and Surface Finshing 69(6), 86, 1982

    被引用文献1件

  • <no title>

    WILD M. J.

    Plating and Surface Finishing 70(11), 32, 1983

    被引用文献1件

  • <no title>

    P&SF Report

    Plating and Surface Finishing 71(5), 26, 1984

    被引用文献1件

  • <no title>

    青谷薫

    合金めっき3版 4, 1970

    被引用文献1件

  • <no title>

    BAUMGARTNER M. E.

    Metalloberflache 41(11), 559, 1987

    被引用文献1件

  • <no title>

    TYRRELL C. J.

    Trans. Inst. MetalFinishing 45, 53, 1967

    被引用文献1件

  • <no title>

    WIESNER Harold J.

    U. S. Pat. 3,923,612, 1975

    被引用文献2件

  • <no title>

    BRENNER Abner

    Plating 52(12), 1249, 1965

    被引用文献2件

  • <no title>

    KROHN A.

    Plating 58(3), 237, 1971

    被引用文献1件

  • <no title>

    THOMS W. A.

    British Pat. 7853, 1894

    被引用文献1件

  • <no title>

    尾崎萃

    貴金属元素の化学と応用 422, 1984

    被引用文献2件

  • <no title>

    電気化学協会偏

    電気化学便覧 122, 1985

    被引用文献1件

  • <no title>

    松本誠臣

    金属表面技術 14(7), 253, 1963

    被引用文献1件

  • <no title>

    HANSEN M.

    Constitution of Binary Alloys 1141, 1958

    被引用文献1件

  • <no title>

    電気鍍金研究会編

    機能めっき皮膜の物性 7, 1986

    被引用文献2件

各種コード

  • NII論文ID(NAID)
    10002260242
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    4334601
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ