高強度Al-TM-Ln系急冷凝固粉末の成形固化および材料特性 Consolidation and Mechanical Properties of High Strength Rapidly Solidified Al-TM-Ln Alloy Powder

この論文にアクセスする

この論文をさがす

著者

    • 大槻 真人 OTSUKI Masato
    • 三菱マテリアル(株)総合研究所材料技術研究所 Materials Research Laboratories, Central Research Institute, Mitsubishi Materials Corporation
    • 由利 浩一 YURI Koichi
    • 三菱マテリアル(株)総合研究所材料技術研究所 Materials Research Laboratories, Central Research Institute, Mitsubishi Materials Corporation
    • 河野 通 [他] KOHNO Tohru
    • 三菱マテリアル(株)総合研究所材料技術研究所 Materials Research Laboratories, Central Research Institute, Mitsubishi Materials Corporation

抄録

Rapidly solidified AI-TM-Ln base alloy has excellent mechanical properties such as high specific strength or specific modulus. In this study, Al<SUB>92</SUB>Ni<SUB>4.5</SUB>Ti<SUB>1.5</SUB>CulZr<SUB>0.8</SUB>Ce<SUB>0.2</SUB> (at%) alloy powders were directly forged using a double action forging press without preparing a compact preform that is difficult to consolidate because of the spherical shape and hardness of the powder. The tensile strength of above test pieces preheated at 723K for 3600s shows 670MPa and 2% elongation, which is comparable with the test pieces prepared by extrusion from the same powder. This process gives near net shape parts with excellent mechanical properties using the rapidly solidified Al-TM-Ln base alloy.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 43(10), 1183-1187, 1996-10-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  5件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002260753
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4057319
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ