Z型マグネトプラムバイトの磁気特性に及ぼすホットプレス及びアンニーリング温度の影響 Effects of Hot-Pressing and Annealing Temperature on the Magnetic Properties of Z Type Magnetoplumbite

この論文にアクセスする

この論文をさがす

著者

抄録

The magnetoplumbite ferrite with the composition of 2Co0⋅3Ba<SUB>0.6</SUB>Sr<SUB>0.5</SUB> 0⋅10.8Fe<SUB>2</SUB>O<SUB>3</SUB> was reported to reveal enhanced dispersion frequency.<BR>This paper aims to enhance the dispersion frequency of this ferrite, using calcined powder finerly pulverized. The resonance frequency corresponding to μ″ maximum of the sample hot-pressed at 1110 °C in an oxygen atmosphere extendes to 3.4 GHz, which is almost the vale theoretically predicted, although its permeability is only only 4.4. The resonance frequency decreases and the permeability increases with increasing hot-pressing temperature. Moreover annealing of the hot-pressed sample at higher temperature results in almost the same result.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 43(10), 1238-1241, 1996-10-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  3件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002260823
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    SHO
  • ISSN
    05328799
  • NDL 記事登録ID
    4057328
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ