- HIP Sintering and Saturation Magnetization of Fe4N.
- Fe4N ノ HIP ショウケツ ト ショウケツタイ ノ ジキ トクセイ
この論文をさがす
抄録
Since Fe4N decomposes at 670°C, sintering of Fe4N powder has not been performed under atmospheric pressure. In this study, Fe4N powders have been sintered below the decomposition temperature applying hipping pressure. The sealed capsule containing Fe4N powder was hipped at 450-550°C for 2 hours under 50-200 MPa. The decomposition of Fe4N was confirmed at 550°C. Therefore, hipping temperature was restricted below 500°C. The maximum relative density 97% was obtained for the specimen hipped at 500°C under the maximum pressure of 200MPa. The specimen obtained at 450°C has a higher saturation magnetization than that obtained at 500°C. The maximum saturation magne-tization 182emu/g was measured for a specimen obtained at 450°C under 200 MPa. The saturation magnetization was decreased to 151 emu/g by the addition of small amount of oxygen (0.33wt%) to Fe4N raw powder. In addition, the corrosion resistance of the hipped Fe4N was higher than that of steel.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 43 (12), 1415-1419, 1996
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206309060352
-
- NII論文ID
- 10002261164
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4118676
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可