SiC粒子分散によるムライトの高温強度特性の向上 Improvement of High Temperature Strength of Mullite by Dispersion of SiC Particles

この論文にアクセスする

この論文をさがす

著者

抄録

Mullite/SiC composite ceramics containing 20 vol% SiC particles (0.12-1.71μm) were prepared by hot-pressing at 1650°C under 35 MPa for 4h. The effect of SiC particle size on mechanical properties such as bending strength and plastic deformation behavior at high temperatures was investigated as a function of cross-head speed. Bending strength and yield stress of mullite/SiC composite ceramics were higher than those of monolithic mullite at high temperatures. Bending strength and yield stress at 1300°C decreased with decreasing cross-head speed. At 1300°C, mullite/SiC composite ceramics with SiC grain size of 0.56-0.76 μm showed the highest bending strength and yield stress, which are 30-80% higher than those of monolithic mullite. On the other hand, mullite/SiC composite ceramics with SiC grain size of 0.18 μm showed maximum plastic deformation.

収録刊行物

  • 粉体および粉末冶金

    粉体および粉末冶金 43(12), 1429-1434, 1996-12-15

    Japan Society of Powder and Powder Metallurgy

参考文献:  6件中 1-6件 を表示

  • <no title>

    秋ヤスヨシ

    日本機械学会論文集(A編) 60, 2829, 1994

    被引用文献1件

  • <no title>

    佐藤繁美

    日本機械学会論文集(A編) 61, 1023, 1995

    被引用文献3件

  • <no title>

    CHU M. C.

    Fatigue Fract. Engng Mater. Struct. 18, 1019, 1995

    被引用文献1件

  • <no title>

    日本規格協会

    JIS規格 R1601

    被引用文献1件

  • <no title>

    KUBOTA Y. and TAKAGI H.

    Brit. Ceram. Proc. 37, 179, 1986

    被引用文献1件

  • <no title>

    大西宏司

    日本セラミックス協会論文誌 98, 541, 1990

    被引用文献1件

各種コード

  • NII論文ID(NAID)
    10002261191
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    4118678
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ