高純度ムライトの泥漿鋳込成形とその焼結体の特性(第2報) -真空ろ過成形と焼結体の機械的特性- [in Japanese] Slip Casting of Mullite and Properties of Sintered Body(Part2)-Vacuum Pressure Assisted Slip Casting and Mechanical Properties of Sintered Body- [in Japanese]
Access this Article
Search this Article
Slip casting of high purity mullite powder produced by coprecipitation method was studied to fabricate mullite ceramic parts with complicated shapes. The preparation conditions of well dispersed slurry (71mass% solids) was prepared by addition of deflocculant (0.2mass%), binder (0.3mass%) and defoamer (0.15mass%). Shaping of test pieces were used by the vaccum pressure assisted slip casting system with a porous polymer resin mold. The mechanical properties of the sintered body were investigated. High density mullite ceramics was obtained at 1650°C for 5hr. The sintered body of high purity mullite showed a flexural strength of about 290MPa and a Weibull modulus of 20.0 at room temperature.
- J. Jpn. Soc. Powder Powder Metallurgy
J. Jpn. Soc. Powder Powder Metallurgy 44(11), 1061-1064, 1997-11-15
Japan Society of Powder and Powder Metallurgy