In Situ Observation of Electrochemical Formation and Degradation Processes of Polyaniline by Fourier-Transform Infrared Spectroscopy.
-
- NAKAYAMA Masaharu
- Department of Applied Chemistry, Yamaguchi University
-
- SAEKI Seigo
- Department of Applied Chemistry, Yamaguchi University
-
- OGURA Kotaro
- Department of Applied Chemistry, Yamaguchi University
この論文をさがす
抄録
The electrochemical polymerization of aniline on a platinum electrode in aqueous HClO4 and H2SO4 solutions has been studied by means of in situ Fourier-transform infrared (FTIR) reflection spectroscopy. The spectra, taken at early stage of the polymerization in both solutions, exhibited the absorption characteristic of polyaniline (PAn) in an emeraldine state, even at a highly positive potential (≥+0.7 V vs. Ag/AgCl (saturated KCl)). Polymer growth in H2SO4 was accompanied by an increase in the molar ratio of [HSO4-]/[SO42-], indicating that the protons generated during the oxidation of aniline react with SO42- to afford HSO4-, and that polymer growth is facilitated. In contrast, such proton-scavenging behavior was not observed in a HClO4 solution, and the growth of PAn was suppressed owing to the accumulation of protons. Under the condition that aniline was extremely consumed, the produced PAn was subjected to oxidative degradation, which was competitive with the growth process of PAn. The major degradation species was identified to be p-benzoquinone.
収録刊行物
-
- Analytical Sciences
-
Analytical Sciences 15 (3), 259-263, 1999
社団法人 日本分析化学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390282679229950976
-
- NII論文ID
- 130004440027
- 10002419107
-
- NII書誌ID
- AA10500785
-
- COI
- 1:CAS:528:DyaK1MXhvVOgtLY%3D
-
- ISSN
- 13482246
- 09106340
-
- NDL書誌ID
- 4810281
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可