Diffusion Brazing of Short Al<SUB>2</SUB>O<SUB>3</SUB> Fiber-Reinforced Aluminum Composite

DOI Web Site 被引用文献1件 参考文献6件
  • Suzumura Akio
    Department of Mechanical Engineering for Production, Tokyo Institute of Technology
  • Xing Yujin
    Department of Mechanical Engineering for Production, Tokyo Institute of Technology

この論文をさがす

抄録

By using of the eutectic reaction of siver and aluminum, short Al2O3 fiber reinforced Al composite(Al2O3/Al FRM) was diffusion-brazed in vacuum at 853K with 0.1mm or 0.01mm thick silver foil as interlayer. Effects of melting of the FRM matrix by the interlayer, discharge of the liquid from the joint area by joining pressure, and diffusion of the liquid into the matrix on the structure and strength of joint were investigated.<BR>With the joining time increasing, the residue of interlayer decreased and the joint strength increased. However, after the solidification of joint area, the fiber segregation occured at the center of joint and the strength of joint decreased. Higher strength of joint was got with intermittent residue of melted reaction layer existing in the joints. Higher joining pressure discharged the melted interlayer out of joints, which would make the fiber segregate in the joint, and the strength of joint became lower than that made with lower joining pressure. Al2O3/Al FRM joints fabricated with 0.01mm silver foil had only a very low strength because during heating period the silver interlayer diffused into base metal and the amount of liquid in joints were not enough to remove the oxide film off the surface to be joined.

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ