Soft Magnetic Properties and Wide Supercooled Liquid Region of Fe–P–B–Si Base Amorphous Alloys
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
-
- Park Rae Eun
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Soft Magnetic Properties and Wide Supercooled Liquid Region of Fe–P–B–Si Base Amorphous Alloys
- Soft Magnetic Properties and Wide Super
この論文をさがす
抄録
The glass transition phenomenon was observed in the temperature range before crystallization for amorphous Fe80(P, B, Si)20 alloys. The temperature interval of the supercooled liquid region (ΔTx) is defined by the difference between glass transition temperature (Tg) and crystallization temperature (Tx) and the largest ΔTx(=Tx−Tg) value is 36 K for Fe80P12B4Si4 where the crystallization reaction takes place through a single stage. The ΔTx value increases by the dissolution of Al and/or Ga and the largest value is 46 K for Fe76Al4P12B4Si4 and 49 K for Fe74Al4Ga2P12B4Si4. The effectiveness of additional Al and/or Ga elements is interpreted to result from the formation of a higher degree of dense random packed structure by dissolving the Al and Ga elements with larger atomic sizes. These Fe-based amorphous alloys exhibiting the glass transition phenomenon crystallize through a single-stage exothermic reaction due to the precipitation of five crystalline phases α-Fe, Fe3B, Fe2B, Fe3P and FeP. The long-range atomic rearrangement necessary for the nearly simultaneous precipitaion of the five crystalline phases seems to cause the appearance of the supercooled liquid region through the retardation of the precipitation reaction. The Fe-based amorphous alloys exhibit good soft magnetic properties of 1.14 to 1.34 T for saturation magnetization, 1.1 to 6.4 A/m for coercive force and 19000 to 22000 for permeability at 1 kHz in the annealed state for 600 s at 723 K. The synthesis of the Fe-based amorphous alloys exhibiting good soft magnetic properties and a wide supercooled liquid region is important for future development of a new type of soft magnetic material.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 37 (11), 1715-1721, 1996
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204248336896
-
- NII論文ID
- 130003556599
- 10002451102
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK2sXntFKmtg%3D%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4090719
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可