Structure at Near-Surface of TiN-Coated Grain Oriented Silicon Steel Sheet Characterized by Ultra-Low Iron Loss
-
- Inokuti Yukio
- Research Laboratories, Kawasaki Steel Corp.
書誌事項
- タイトル別名
-
- Structure at Near-Surface of TiN Coated
この論文をさがす
抄録
The mechanism responsible for ultra-low iron loss in TiN-coated silicon steel sheet was clarified by electron microscope observation of the magnetic domain and the structure at the interface of the TiN film and single crystal of silicon steel, and by X-ray pole figure measurement. Marked domain refinement due to thin TiN film coating was accomplished, satisfying the coherency relationship of (1\bar11)TiN//(011)Si-steel, [110]TiN//[100]Si-steel between the TiN film and single crystal matrix, by applying a strong surface tension to the [100]Si-steel direction (elastic strain along only one axis). Fine transverse fringes were observed at the interface using a transmission electron microscope, and the elliptical shape of the {200}Si-steel pole peaks was detected by measuring the dual textures of X-ray pole figures.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 38 (3), 266-274, 1997
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204247123200
-
- NII論文ID
- 130003556907
- 10002452172
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK2sXjtVOhsrg%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4209544
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可