Thermal Evolution Spectrum of Hydrogen from Low Carbon Steel Charged by Cathodic Polarization

DOI Web Site Web Site 60 References
  • Hagi Hideki
    Department of Mechanical Engineering, Fukui University of Technology

Bibliographic Information

Other Title
  • Thermal Evolution Spectrum of Hydrogen

Search this article

Abstract

The introduction of large amounts of hydrogen into low-carbon steel specimens by cathodic polarization produces hydrogen damage such as blisters, microcracks and dislocations. Hydrogen exists in the specimens as atoms dissolved in the iron lattice, as atoms trapped at lattice defects such as dislocations, and as gas precipitated in void defects such as blisters and microcracks. Hydrogen detected by electrochemical permeation in annealed specimens is one dissolved in the lattice, and the majority of hydrogen detected by glycerol displacement is the precipitated molecular hydrogen. In annealed specimens, a single peak is observed in the thermal evolution spectrum. This peak originates from the evolution of precipitated hydrogen, and the peak temperature depends on the specimen thickness, hydrogen concentration and heating rate. In cold-rolled specimens, two peaks are observed. The lower temperature peak originates from the evolution of precipitated hydrogen and the higher temperature peak from the trapped hydrogen.

Journal

References(60)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top