Effect of Boron Addition on Microstructure and Properties of Sintered Fe-1.5Mo Powder Materials.
-
- Dudrová Eva
- Institute of Materials Research of Slovak Academy of Sciences
-
- Selecká Marcela
- Institute of Materials Research of Slovak Academy of Sciences
-
- Burea Radovan
- Institute of Materials Research of Slovak Academy of Sciences
-
- Kabátová Margita
- Institute of Materials Research of Slovak Academy of Sciences
この論文をさがす
抄録
The microstructure formation and mechanical properties of sintered materials based on the prealloyed Fe-1.5wt%Mo powder with 0.2-0.6 wt% of boron addition are investigated.An eutectic liquid phase Fe+Fe2B activating the sintering of Fe-1.5Mo+B powder systems is formed. Besides this, an interaction of boron with the Fe-Mo prealloyed matrix occured and the formation of fine particles containing molybdenum and boron was registered. Due to this interaction the decrease of eutectic phase portion and strengthening of the matrix by borides was occurred. The materials Fe-1.5Mo+0.4wt%B achieved the tensile strength Rm=487 MPa, the elongation A5=2.5 % and the hardness of 212 HV 30 at the density of 7.15 g·cm-3 after sintering at 1 200° for 30 min.
収録刊行物
-
- ISIJ International
-
ISIJ International 37 (1), 59-64, 1997
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681429324544
-
- NII論文ID
- 10002454739
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可