Effect of Cu, Sn and Ni on Hot Workability of Hot-rolled Mild Steel

この論文にアクセスする

この論文をさがす

著者

抄録

The effect of tramp elements Cu and Sn on the hot workability of mild steels was investigated in this paper. A hot rolling condition was simulated by oxidizing followed by tensile-deforming and the hot workability was assessed by measuring the number of surface cracks. The microstructure at the scale/steel interface was closely observed, and the relationship between the surface cracking and the microstructure was established.<br> Sn as low as 0.04 % increased the number of cracks in an 0.3 % Cu bearing steel, while 0.3 % Ni suppressed the cracking in an 0.3%Cu-0.04%Sn bearing steel. An energy dispersive X-ray spectroscopy (EDX) at the subscale layer of the oxidized Cu-Sn bearing steel revealed that an 82%Cu-7%Sn-Fe alloy phase formed at the scale/steel interface. The phase calculation using the Thermo-Calc computer program showed that Sn decreased the solubility limit for Cu in Fe, thus increasing the amount of liquid Cu enriched alloy and enhancing the surface cracking by Cu liquid embrittlement.<br> On the other hand, an addition of 0.3 % Ni to the 0.3%Cu-0.04%Sn bearing steel formed two different Cu-Sn phases at the surface of the steel; a 12%Cu-19%Ni-Fe layer under the steel surface and a liquid 63%Cu-12%Sn-12%Ni-Fe alloy placed above the layer. The amount of the 63%Cu-Sn-Ni-Fe alloy was a little, and the 12%Cu-Ni-Fe layer was in a large amount. In addition, the phase calculation at an oxidation temperature 1 100°C showed that the Cu and Ni enriched layer was solid. Therefore, the addition of 0.3 % Ni suppressed the surface cracking in the Cu-Sn bearing steel. A mechanism of the reduced amount of liquid by increasing Ni content was discussed in terms of local equilibrium and inward diffusion of Cu atoms from the Cu enriched layer into the steel.

収録刊行物

  • ISIJ international

    ISIJ international 37(3), 217-223, 1997-03-15

    The Iron and Steel Institute of Japan

参考文献:  13件中 1-13件 を表示

  • <no title>

    BORN K.

    Stahl Eisen 73, 1268, 1953

    被引用文献11件

  • <no title>

    NICHOLSON A.

    J. Iron Steel Inst. 203, 1007, 1965

    被引用文献15件

  • <no title>

    MAY I. L.

    Copper in Iron and Steel, 1982

    被引用文献6件

  • <no title>

    AKAMATU S.

    CAMP-ISIJ 7, 1712, 1994

    被引用文献1件

  • <no title>

    KAJITANI T.

    Tetsu-to-Hagane 81, 185, 1995

    被引用文献16件

  • <no title>

    SUZUKI H.

    CAMP-ISIJ 8, 1391, 1995

    被引用文献2件

  • <no title>

    SEO S.

    CAMP-ISIJ 8, 1392, 1995

    被引用文献2件

  • <no title>

    MATSUOKA H.

    CAMP-ISIJ 8, 1395, 1995

    被引用文献3件

  • <no title>

    NAGASAKI C.

    CAMP-ISIJ 8, 1396, 1995

    被引用文献3件

  • <no title>

    IMAI N.

    ISIJ Int. 37, 224, 1997

    被引用文献13件

  • <no title>

    OIKAWA H.

    Tetsu-to-Hagane 68, 1489, 1982

    被引用文献6件

  • <no title>

    IMADA F.

    CAMP-ISIJ 7, 886, 1994

    被引用文献1件

  • The Thermo-Calc databank system

    SUNDMAN B.

    CALPHAD 9(2), 153-190, 1985

    DOI 被引用文献185件

被引用文献:  14件中 1-14件 を表示

各種コード

ページトップへ