Effects of Cu and Other Tramp Elements on Steel Properties. Influence of Cu and Sn on Hot Ductility of Steels with Various C Content.
-
- Matsuoka Hideki
- Materials and Processing Research Center, NKK Corporation
-
- Osawa Koichi
- Materials and Processing Research Center, NKK Corporation
-
- Ono Moriaki
- Materials and Processing Research Center, NKK Corporation
-
- Ohmura Masanori
- Materials and Processing Research Center, NKK Corporation
この論文をさがす
抄録
The influence of Cu and Sn on the hot ductility at the strain rate of 10-3 s-1 for steels with C contents from 0.002 to 0.15 mass% was investigated. The hot ductility dropped at austenite+ferrite two phase region just below A3, namely, 800 to 900°C. The hot ductility deteriorated more at higher C content, and furthermore with the co-addition of Cu and/or Sn. It was considered that the deterioration at austenite+ferrite two phase region in the Cu, Sn bearing steel was caused by the combined effect of following factors: (1) the formation of proeutectoid ferrite along the austenite grain boundaries, (2) the segregation of Sn at the interface between proeutectoid ferrite and austenite or at the austenite grain boundaries, and (3) the increase in the difference of the deformation strength between austenite and proeutectoid ferrite.
収録刊行物
-
- ISIJ International
-
ISIJ International 37 (3), 255-262, 1997
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206453584128
-
- NII論文ID
- 10002455241
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可