The δ to γ Transition in Fe-Cr-Ni Alloys during Laser Treatment

この論文にアクセスする

この論文をさがす

著者

    • FUKUMOTO Shigeo
    • Department of Materials, Swiss Federal Institute of Technology Lausanne(EPFL)
    • KURZ Wilfried
    • Department of Materials, Swiss Federal Institute of Technology Lausanne(EPFL)

抄録

Laser remelting experiments have been performed with Fe-18%Cr-Ni alloys to evaluate the effects of composition (Cr/Ni ratios between 1.30 and 1.83) and growth velocity (0.9 to 50 mm/s) on the microstructure selection during solidification between primary δ-ferrite and primary γ-austenite. The experimental results are compared with theoretical predictions from a dendrite growth model. The experimental transitions from ferrite to austenite are in good agreement with theory for both an increase in Ni content and increase in growth rate. The transitions from austenite to ferrite are found to occur at lower Ni contents than predicted. It is thought that the δ-γ transition shows no nucleation barrier and is controlled by dendrite growth kinetics and the γ-δ transition is controlled by nucleation of ferrite.

収録刊行物

  • ISIJ international  

    ISIJ international 37(7), 677-684, 1997-07-15 

    The Iron and Steel Institute of Japan

参考文献:  24件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

ページトップへ