Infiltration of Microporous Activated Charcoal by Pyrolysis of CH4 and Its Effect on Enhancement of Resistance against Oxidation.
-
- Shigeno Yoshihito
- Graduate School of International Cultural Studies, Tohoku University
-
- Evans James William
- Department of Materials Science and Mineral Engineering, University of California
-
- Yoh Itsumei
- Coulter Japan Scientific Instruments Company, Ltd
この論文をさがす
抄録
Pores within activated charcoal (A.C.) were infiltrated by pyrolitic carbon derived from thermal decomposition of CH4. The infiltrated activated charcoal showed an increase in resistance against oxidation with CO2. To elucidate the mechanism of this effect, the pore size distribution of macropores, mesopores and micropores including submicropores were characterized for the original A.C., infiltrated A.C., oxidized A.C. and A.C. oxidized after infiltration, respectively. It was found that the infiltration decreased the volume and the surface area of pores, particularly the surface area of micropores.<br> When oxidized, the carbon which deposited in macropores is almost burned but that in meso- and micropores is only partly burned; The ratio of increase in surface area of the infiltrated sample is smallest for the micropores. From these experimental results, it is deducible that the deposited carbon in micropores plays the major role for blocking CO2 intruding, thereby the resistance against oxidation is enhanced.
収録刊行物
-
- ISIJ International
-
ISIJ International 37 (8), 738-747, 1997
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206452151680
-
- NII論文ID
- 10002456507
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可