Recrystallization-induced Precipitation Interaction in a Medium Carbon Vanadium Microalloyed Steel.

DOI Web Site 2 Citations 23 References
  • Quispe A.
    Centro Nacional de Investigaciones Metalúrgicas (CENIM-CSIC)
  • Medina S. F.
    Centro Nacional de Investigaciones Metalúrgicas (CENIM-CSIC)
  • Valles P.
    Instituto Nacional de Técnica Aeroespacial (INTA)

Search this article

Abstract

Using torsion tests, a study has been made of Recrystallization-Precipitation (R-P) interaction in a vanadium microalloyed steel for two strains (0.20 and 0.35). When strain induced precipitation starts, the recrystallized fraction deviates from Avrami's equation, giving rise to the formation of a plateau on the curves which represent the recrystallized fraction against time. This makes it possible to know the moment at which precipitation starts (Ps) and the moment at which it finishes (Pf). After the end of precipitation, recrystallization continues to progress in accordance with Avrami's law. Recrystallization-Precipitation-Time-Temperature (RPTT) diagrams have been drawn, superposing on them the lines corresponding to different recrystallized fractions. This makes it possible to represent in graph form the Recrystallization-Precipitation interaction and the determination of the static recrystallization critical temperature (SRCT). It is demonstrated that during the interval of time in which precipitation occurs (Pf - Ps), recrystallization does not advance. The work which has been carried out establishes new aspects in the phenomenon of R-P interaction.

Journal

  • ISIJ International

    ISIJ International 37 (8), 783-788, 1997