Activities of FeO in CaO-Al2O3-SiO2-FeO and CaO-Al2O3-CaF2-FeO Slags.
-
- Taniguchi Yoshinori
- Department of Metallurgy, The University of Tokyo
-
- Morita Kazuki
- Department of Metallurgy, The University of Tokyo
-
- Sano Nobuo
- Department of Metallurgy, The University of Tokyo
Search this article
Abstract
Activity coefficients of FeO in molten CaO-Al2O3-SiO2-FeO (<5 %) slags were determined at 1673 and 1873 K by equilibrating the slags with copper-iron alloys in a controlled oxygen partial pressure (PO<sub>2</sub>=5.71×10-12 atm at 1673 K, 1.90×10-10 atm at 1873 K). Activity coefficients of iron in copper-iron (<4 %) alloys at 1673 K were preliminarily determined by controlling the activity of iron using FeO·Cr2O3 saturated with Cr2O3 in a various oxygen partial pressures (PO<sub>2</sub>=3.66×10-12-9.14×10-11 atm). <br>It was found that the activity coefficients of FeO obey Henry's law, and have the maximum value when the ratio of NCaO/NSiO<sub>2</sub> is about 2 at a constant Al2O3 content. The activity coefficients of iron in copper-iron alloy referred to pure liquid were determined as<br><br>lnγFe=2.76-11.3NFe.<br><br>The effect of a CaF2 addition to the CaO-Al2O3-FeO system on the activity coefficient of FeO was also investigated at 1723 K.
Journal
-
- ISIJ International
-
ISIJ International 37 (10), 956-961, 1997
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681428880000
-
- NII Article ID
- 10002457104
-
- NII Book ID
- AA10680712
-
- COI
- 1:CAS:528:DyaK2sXnslyrurg%3D
-
- ISSN
- 13475460
- 09151559
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed