Interconnected network of AlN/Al composites are produced by in situ liquid metal-gas reactions. In this study, various Al-Si-Mg alloys are nitrided in N2-4 %H2 atmosphere to understand the composite growth mechanism. Both fibre and particulate SiC reinforcements are infiltrated with AlN/Al reaction product to form near dense composites and mechanical properties are compared with those of AlN particulate reinforced AlN/Al composite. The composite microstructure is found to be sensitive to the processing temperature, alloy composition and filler material size and chemistry. The variation in mechanical property is also dependent on the residual porosity. Formation of moisture sensitive Al4C3 in SiC reinforced composites causes deterioration of mechanical properties. Various alternatives to prevent Al4C3 formation are discussed in the text.
収録刊行物
-
- ISIJ International
-
ISIJ International 37 (10), 992-999, 1997
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681428904448
-
- NII論文ID
- 10002457185
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可