- Okane Toshimitsu
- Department of Metallurgy, Graduate School of Engineering, The University of Tokyo
-
- Umeda Takateru
- Department of Metallurgy, Graduate School of Engineering, The University of Tokyo
この論文をさがす
抄録
In this report, transition of solidified phases in unidirectionally solidified Fe–Cr–Ni alloys was investigated in low growth rate range using Bridgman type furnace. The ferrite-austenite eutectic growth was confirmed under low growth rate condition like a plane front growth of ferrite single phases. The transition velocity between eutectic and ferrite cell growth had a good agreement with the result of calculation based on the phase selection criterion and the interface temperature calculation for ferrite, austenite and eutectic phases. These results show that the phase prediction by calculating interface temperature can be applied not only to competitive growth between single phases like peritectic systems, but also to eutectic systems. Furthermore, under the condition of eutectic coupled growth to be occurred in steady state, the changes of solidified phases and their morphologies in the initial transient are also discussed.
収録刊行物
-
- ISIJ International
-
ISIJ International 38 (5), 454-460, 1998
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206451953792
-
- NII論文ID
- 10002459437
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可