Recrystallization and Related Phenomena. Recrystallization-Transformation Combined Reactions during Annealing of a Cold Rolled Ferritic-Austenitic Duplex Stainless Steel.
-
- Reick Wolfgang
- Department of Mechanical Engineering, University of São Paulo
-
- Pohl Michael
- Institute for Materials, Faculty of Mechanical Engineering, Ruhr-University
-
- Padilha Angelo Fernando
- Department of Metallurgical and Materials Engineering, University of São Paulo
この論文をさがす
抄録
Solid state reactions taking place during annealing of 20% cold rolled ferrite–austenite duplex stainless steel (DIN W.-Nr: 1.4462) have been studied by means of several complementary techniques: optical, scanning and transmission electron microscopy, X-ray diffraction analysis, microhardness and ultramicrohardness measurements and magnetic phase detection (ferritoscope). It has been found that after cold rolling austenite exhibited more strain hardening and a higher driving force for recrystallization than ferrite. Extensive recovery took place in ferrite during annealing, while the deformation substructure of austenite remained nearly unrecovered until beginning of recrystallization. The recrystallization kinetics in ferrite was faster than in austenite. Recrystallization in austenite occurred in a more discontinuous manner than in ferrite. The eutectoid transformation of ferrite to sigma phase plus austenite slowed down recrystallization kinetics of both ferrite and austenite phases. A scheme is presented for sigma phase formation during recrystallization annealing.
収録刊行物
-
- ISIJ International
-
ISIJ International 38 (6), 567-571, 1998
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206452883840
-
- NII論文ID
- 10002459766
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DyaK1cXkvVyquro%3D
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可