Texture Evolution of IF Steel Due to Recrystallization

この論文にアクセスする

この論文をさがす

著者

抄録

The evolution of texture due to recrystallization was investigated in cold rolled Ti-bearing IF steel sheets using Electron Back Scattering Pattern (EBSP). The aim of this study was to obtain a real picture of the formation of the recrystallization texture of IF steel sheets, which would contribute to proper texture control for improving deep drawability.<br> The deformed grains can be roughly classified by the following 5 orientation groups: (1) ND//<111> and RD//<112>∼<110>, (2) ND//<111>∼<335> and RD//<110>, (3) around {112} <110>, (4) around {001} <110> and (5) widely scattered orientations. Their ratios of frequency of finding are approximately 12 : 4 : 4 : 5 : 2. Deformed grains of types (1) and (5) recrystallized at the early stage of recrystallization. The nucleation sites are both grain boundaries and grain interior. The orientations of grains recrystallized from a grain of type (1) are ND//<111> and RD//<112>∼<110> while the orientations of grains recrystallized from a grain of type (5) are widely scattered. Most of the deformed grains of types (2), (3) and (4) recrystallized at the later stage of recrystallization. The recrystallization of these grains of types progresses through the growth of already recrystallized neighboring grains if the neighboring grains are types (1) and (5). There exist no preferential misorientation axes for migrating recrystallization fronts. Most of the misorientation angles lie between 20º and 55º.

収録刊行物

  • ISIJ international  

    ISIJ international 38(6), 617-624, 1998-06-15 

    The Iron and Steel Institute of Japan

参考文献:  20件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

ページトップへ