Recrystallization and Related Phenomena. Texture Evolution of IF Steel Due to Recrystallization.
-
- Hashimoto Natsuko
- Steel Research Laboratories, Nippon Steel Corporation
-
- Yoshinaga Naoki
- Steel Research Laboratories, Nippon Steel Corporation
-
- Senuma Takehide
- Steel Research Laboratories, Nippon Steel Corporation
Search this article
Abstract
The evolution of texture due to recrystallization was investigated in cold rolled Ti-bearing IF steel sheets using Electron Back Scattering Pattern (EBSP). The aim of this study was to obtain a real picture of the formation of the recrystallization texture of IF steel sheets, which would contribute to proper texture control for improving deep drawability.<br> The deformed grains can be roughly classified by the following 5 orientation groups: (1) ND//<111> and RD//<112>∼<110>, (2) ND//<111>∼<335> and RD//<110>, (3) around {112} <110>, (4) around {001} <110> and (5) widely scattered orientations. Their ratios of frequency of finding are approximately 12 : 4 : 4 : 5 : 2. Deformed grains of types (1) and (5) recrystallized at the early stage of recrystallization. The nucleation sites are both grain boundaries and grain interior. The orientations of grains recrystallized from a grain of type (1) are ND//<111> and RD//<112>∼<110> while the orientations of grains recrystallized from a grain of type (5) are widely scattered. Most of the deformed grains of types (2), (3) and (4) recrystallized at the later stage of recrystallization. The recrystallization of these grains of types progresses through the growth of already recrystallized neighboring grains if the neighboring grains are types (1) and (5). There exist no preferential misorientation axes for migrating recrystallization fronts. Most of the misorientation angles lie between 20º and 55º.
Journal
-
- ISIJ International
-
ISIJ International 38 (6), 617-624, 1998
The Iron and Steel Institute of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681427871616
-
- NII Article ID
- 10002459914
-
- NII Book ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed