Recrystallization and Related Phenomena. Effect of Lubrication Condition on Recrystallization Texture of Ultra-low C Sheet Steel Hot-rolled in Ferrite Region.
-
- Matsuoka Saiji
- Iron and Steel Research Laboratories, Kawasaki Steel Corporation
-
- Morita Masahiko
- Iron and Steel Research Laboratories, Kawasaki Steel Corporation
-
- Furukimi Osamu
- Iron and Steel Research Laboratories, Kawasaki Steel Corporation
-
- Obara Takashi
- Iron and Steel Research Laboratories, Kawasaki Steel Corporation
Search this article
Abstract
The application of the EBSD technique with an SEM provides a new approach to the analysis of variations of the recrystallization texture in the thickness direction of ultra-low carbon sheet steels rolled in the ferrite region. A nonuniform recrystallization texture through the thickness is formed due to the additional shear strain introduced by frictional force between the rolls and the material in sheet steel rolled with a friction coefficient over 0.15, <110>//ND recrystallized grains being formed near the surface, and <111>//ND and <100>//ND recrystallized grains being formed at the mid plane. On the other hand, <110>//ND recrystallized grains are not formed preferentially near the surface, and <111>//ND and <100>//ND recrystallized grains are formed uniformly throughout the thickness in sheet steel rolled with a friction coefficient under 0.15. Orientation imaging also reveals differences related to the tolerance of <110>//ND recrystallized grains around the <110>//ND axis in sheet steel rolled without lubrication, in that <110>//ND grains with a small tolerance form at the 1/10 plane from the surface and <110>//ND grains with larger tolerances form at thickness locations from the 1/10 plane toward the surface and center. The r-value depends on the friction coefficient and increases significantly as the friction coefficient decreases under 0.15, resulting in high r-values over 1.2. This change in the r-value with the friction coefficient corresponds to the distribution of the recrystallization texture through the thickness. Orientation imaging allows a more visual and intuitive understanding of the nonuniformity of the recrystallization texture than conventional methods such as optical microscopy and X-ray diffraction measurement.
Journal
-
- ISIJ International
-
ISIJ International 38 (6), 633-639, 1998
The Iron and Steel Institute of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206452901120
-
- NII Article ID
- 10002459959
-
- NII Book ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed