Determination of aluminum and oxygen contents in liquid iron in equilibrium with α-alumina and hercynite
-
- Wasai Kyoko
- Department of Materials Science and Engineering, Kyushu Institute of Technology
-
- Mukai Kusuhiro
- Department of Materials Science and Engineering, Kyushu Institute of Technology
-
- Fuchiwaki Hidetoshi
- Corporate Semiconductor Component Division, Kawauch-Sendai Plant, Kyocera Corporation
-
- Yoshida Akihiko
- Production Engineering Center, JATCO Corporation
書誌事項
- タイトル別名
-
- Determination of Aluminum and Oxygen Contents in Liquid Iron in Equilibrium with .ALPHA.-Alumina and Hercynite.
この論文をさがす
抄録
The constitution of Al and O at 1873 K at the coexisting point, at which the Fe-Al-O system was in equilibrium with both of FeO·Al2O3 and α-Al2O3, was investigated, and the measured Al and O contents were found to be 0.072 mass% O and 0.0018 mass% Al. The O content of this point agrees well with other measured values. The Al content of this point is two orders of magnitude larger than the activity of Al but agrees fairly well with the Al content predicted by an associated solution model and that measured by Novokhatskiy et al. This result reveals that the equilibrium curve (E.C.), which indicates the Al and O contents in liquid Fe in equilibrium with α-Al2O3, is a concave curve in the low Al region that extends to the coexisting point. However, the E.C. calculated using the interaction parameters and deoxidation constant K is almost a straight line. This discrepancy indicates that the use of the interaction parameters reported for this system is probably inappropriate in the concave E.C. region. The interaction parameters and thermodynamics of this system should be reexamined.
収録刊行物
-
- ISIJ International
-
ISIJ International 39 (8), 760-766, 1999
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681429165952
-
- NII論文ID
- 10002463966
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DyaK1MXmvVCrtrY%3D
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可