炭素繊維/アルミニウム合金複合材料の引張強さおよび圧縮強さに及ぼす界面強さの影響 Effect of Interfacial Shear Strength between Fiber and Matrix on Bending Strength and Compressive Strength of Carbon Fiber Reinforced Aluminium Alloys

この論文にアクセスする

この論文をさがす

著者

抄録

The effect of the interfacial shear strength between the carbon fibers and the matrix of carbon fiber reinforced aluminium alloys (CFRM:two PAN based high modulus and a PAN based high strength CFs, V<SUB>f</SUB>=70%) on the bending strength and the compressive strength has been studied. As the interfacial shear strength increases from a lower level of 5 MPa to a higher level of 25 MPa, the tensile strength of the CFRMs contains high modulus CFs decreases rapidly from a high level of 1, 300 MPa to a low level of 500 MPa. However, as the interfacial shear strengths is varied in this region, the compressive strength of the same CFRM increases sharply from a level of 400 MPa to a level of 1, 600 MPa. The compressive strengths of the CFRMs show a high, constant level of 1, 600 MPa in the range of interfacial shear strengths over 40 MPa. CFRMs with low interfacial shear strengths show fracture at the interface and compressive collapse in compression tests. As the interfacial shear strength of the CFRMs increases, fracture at the interface is reduced, and the probability of shear fracture increases. These changes increase the compressive strengths of the CFRMs. When the level of interfacial shear strength is over 40 MPa and the compressive strengths of the CFRMs exhibit an almost constant level of 1, 600 MPa, in this case the compressive specimens show complete shear fracture mode. The interfacial shear strength is considered to depend on the content of Al<SUB>4</SUB>C<SUB>3</SUB> accumulated at the interface in the CFRMs.

収録刊行物

  • 日本複合材料学会誌 = Journal of the Japan Society for Composite Materials  

    日本複合材料学会誌 = Journal of the Japan Society for Composite Materials 23(1), 12-25, 1997-01-15 

    JAPAN SOCIETY FOR COMPOSITE MATERIALS

参考文献:  34件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002464833
  • NII書誌ID(NCID)
    AN00196748
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03852563
  • NDL 記事登録ID
    4127036
  • NDL 雑誌分類
    ZM16(科学技術--科学技術一般--工業材料・材料試験)
  • NDL 請求記号
    Z14-655
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ