アラミド短繊維充てん多官能性エポキシ樹脂の動力学的性質に及ぼす熱処理と吸水処理の影響 Influence of Aging and Wetting on Dynamic Mechanical Properties of Multi-Functional Epoxy Resins Filled with Aramid Short Fibers

この論文にアクセスする

この論文をさがす

著者

抄録

The composite materials were made from three multi-functional epoxy resins (EP) cured with five hardeners and filled with aramid (Technora®) short fibers (AFP) by 2.44 wt%. Effects of aging (heat-treated) at 130°C for 5, 000 h and wetting at 21°C for 5, 000 h in distilled water on the dynamic mechanical properties were studied. The morphology of the fiber dispersion in AFP-filled specimens did not change during the aging. Weight of the aged specimens decreased for a prolonged aging time. The maximum decrease during the aging for 5, 000h was 3.5wt%. The glass transition temperature (T<SUP>g</SUP>) of all the specimens shifted to higher temperature by the aging. The dynamic storage moduli (E') of most of aged specimens decreased at lower temperature (-140°C) and room temperature (25°C) compared with those of unaged specimens. At higher temperature (200°C), the moduli of specimens almost increased and in particularly those of the specimens cured with diamines increased significantly. Absorbed water of wet specimens reached a maximum value of 5.0wt%, and values of the specimens cured with diamines were larger than those of the specimens cured with acid anhydrides. The T<SUP>g</SUP>of all the specimens shifted to lower temperature by the absorption of water. E' of many wet specimens increased in the range of lower temperature to room temperature, but E' of all the specimens at higher temperature extremely fell down.

収録刊行物

  • 日本複合材料学会誌 = Journal of the Japan Society for Composite Materials  

    日本複合材料学会誌 = Journal of the Japan Society for Composite Materials 23(4), 121-128, 1997-07-15 

    JAPAN SOCIETY FOR COMPOSITE MATERIALS

参考文献:  20件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002465088
  • NII書誌ID(NCID)
    AN00196748
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03852563
  • NDL 記事登録ID
    4256725
  • NDL 雑誌分類
    ZM16(科学技術--科学技術一般--工業材料・材料試験)
  • NDL 請求記号
    Z14-655
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ