Zn_2SiO_4の標準生成ギブズエネルギー Standard Gibbs Energy of Formation of Zn_2SiO_4

この論文にアクセスする

この論文をさがす

著者

抄録

An experimental study was carried out to determine the standard Gibbs energy of formation of zinc orthosilicate, Δ (Zn2SiO4), for the purpose of controlling zinc vapor pressure by utilizing the equilibrium reaction between Zn2SiO4 and a CO-CO2 gas mixture. A CO-CO2 gas mixture of fixed composition was passed through a column of synthesized granular Zn2SiO4 placed in a uniform temperature zone of a furnace, and the equilibrium CO-CO2-Zn(g) gas mixture from the following reaction Zn2SiO4(s) + 2CO(g) = 2Zn(g) + 2CO2(g) + SiO2(s) was contacted with a molten Cu-Zn alloy placed in the same uniform temperature zone, where another equilibrium was made attain between the gas phase and the molten alloy. From the zinc content and the known thermodynamic data of the alloy, pZn in the gas phase was obtained and from which, being combined with the composition of the CO-CO2 gas mixture, pCO and pCO2 were calculated. Those partial pressures were then used to calculate the standard Gibbs energy change of the above reaction, which was combined with the available standard Gibbs energies of formation of CO, CO2, and SiO2 to determine Δ (Zn2SiO4). The result is as follows : Δ (Zn2SiO4) = 0.613T-1,951(±7) (kJ/mol) [1,423-1,573 K]

収録刊行物

  • 資源と素材 : 資源・素材学会誌 : journal of the Mining and Materials Processing Institute of Japan  

    資源と素材 : 資源・素材学会誌 : journal of the Mining and Materials Processing Institute of Japan 114(8), 567-572, 1998-08-25 

    The Mining and Materials Processing Institute of Japan

参考文献:  12件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002467947
  • NII書誌ID(NCID)
    AN10062646
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09161740
  • NDL 記事登録ID
    4555453
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-315
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ