Si-Al-O系の熱力学 Thermodynamics of the Si-Al-O System

この論文にアクセスする

この論文をさがす

著者

抄録

Thermodynamic properties of aluminum in molten silicon were measured by equilibrating silicon melts with mullite(s)-Al2O3(s), mullite(s)-SiO2(s), and SiO2(s) at 1,723 K and 1,773 K.Based on the results, (a) the standard free energy change for the oxygen dissolution into molten silicon, (b) the activity coefficient of aluminum at infinite dilution referred to pure liquid, and (c) the interaction parameters related to aluminum in molten silicon were determined to be:(a) 1/2 O2(g) = (mass%, H, in Si melt):Δ(b) = -1.8(±0.1) (at 1,723 K), = -1.21(±0.01) (at 1,773 K)(c) = 260(±10) (at 1,723 K), = 41(±1) (at 1,773 K eOAl = -0.63(±0.08) (at 1,723 K), eOAl = -0.57(±0.01) (at 1,773 K), respectively, for 1,723 K∼1,773 K.Finally, the stability diagram of the Si-Al-O system was established.

収録刊行物

  • 資源と素材 : 資源・素材学会誌 : journal of the Mining and Materials Processing Institute of Japan  

    資源と素材 : 資源・素材学会誌 : journal of the Mining and Materials Processing Institute of Japan 115(2), 97-102, 1999-02-25 

    The Mining and Materials Processing Institute of Japan

参考文献:  21件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  2件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002469130
  • NII書誌ID(NCID)
    AN10062646
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09161740
  • NDL 記事登録ID
    4662222
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-315
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ