Cr-Ni-N系セラミックス膜の機械的性質 Mechanical Properties of Ceramic Films in the Cr-Ni-N System

この論文にアクセスする

この論文をさがす

著者

    • 安丸 尚樹 YASUMARU Naoki
    • 福井工業高等専門学校機械工学科 Department of Mechanical Engineering, Fukui National College of Technology
    • 真柄 宏之 MAGARA Hiroyuki
    • 福井県工業技術センター新素材開発部 Department of New Material, Fukui Prefectural Industrial Technology Center
    • 伊部 壽夫 IBE Toshio
    • 福井県工業技術センター新素材開発部 Department of New Material, Fukui Prefectural Industrial Technology Center

抄録

Austenitic type 304 stainless steel was ion-nitrided and subsequently ion-plated with CrN or CrNi-N whose Ni content was varied from 11 at% to 50 at%. The ceramic film of CrN coated onto the pre-nitrided steel showed the good wear resistance even under a heavy load. Further, the CrN film with a thickness of 10 μm showed the minimum wear loss among the CrN films of 319 μm. As for the cermet films of CrNi-N composed of Cr<SUP>*</SUP>N and Ni, the CrNi-N film with Ni content of 11 at% coated onto the pre-nitrided steel showed the best wear resistance compared with the CrN film or CrNi-N films with high Ni content. Its good wear resistance was maintained even at the thick film over 20 μm, being different from the tendency of CrN film.

収録刊行物

  • 真空  

    真空 42(3), 159-162, 1999-03 

    The Vacuum Society of Japan

参考文献:  12件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002476193
  • NII書誌ID(NCID)
    AN00119871
  • 本文言語コード
    JPN
  • 資料種別
    SHO
  • ISSN
    05598516
  • NDL 記事登録ID
    4714189
  • NDL 雑誌分類
    ZN15(科学技術--機械工学・工業--流体機械)
  • NDL 請求記号
    Z16-474
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ