固溶強化型Ni基ODS合金におけるY<SUB>2</SUB>O<SUB>3</SUB>-Al<SUB>2</SUB>O<SUB>3</SUB>複合酸化物相の形成

• 西 和也

  株式会社日立製作所日立研究所

• 平野 辰巳

  株式会社日立製作所日立研究所

• 新井 将彦

  株式会社日立製作所日立研究所

• 青野 泰久

  株式会社日立製作所日立研究所

書誌事項

タイトル別名

• Formation of Y<SUB>2</SUB>O<SUB>3</SUB>-Al<SUB>2</SUB>O<SUB>3</SUB> Mixed Oxide Phases in Solid Solution Ni-Base ODS Alloys
• 固溶強化型Ni基ODS合金におけるY2O3-Al2O3複合酸化物相の形成
• コヨウ キョウカガタ Niキ ODS ゴウキン ニ オケル Y2O3-Al2O3 フクゴウ サンカ モッソウ ノ ケイセイ

抄録

A study has been conducted to examine the formation behavior of mixed oxide phases in some solid solution type Ni-base ODS alloys made by MA using TEM, XRD and DTA technique. The results indicate that the mixed oxied YAlO₃ phase, having a hexagonal structure and termed as YAH, formed when heating Ni-20Cr-0.3Al-0.6Y₂O₃(mass%) alloy up to 1173 K. The nano-electron beam diffraction experiments identified that the mixed oxide was uniform in structural aspect. NiO has a facilitative effect on forming YAH type mixed oxide and the ratio of the Y₂O₃ to Al₂O₃ has a profound effect on the crystalline structure type of the mixed oxide. The YAH mixed oxide in Ni-20Cr-0.3Al-0.6Y₂O₃ was stable to higher temperature than that in Ni-5Al-10Y₂O₃-NiO alloys. The present study suggests that the formation and the stability of mixed oxides were strongly affected by the components of ODS alloys and the impurity oxygen absorbed in materials.

収録刊行物

• 日本金属学会誌

  日本金属学会誌 63 (2), 259-268, 1999

  公益社団法人 日本金属学会

キーワード

• oxide dispersion strengthened alloys
• mechanical alloying
• yttrium aluminum mixed oxide phases
• impurity of oxygen

詳細情報

• CRID: 1390282681467400576
• NII論文ID: 10002549005
• NII論文ID: 130007341313
• NII書誌ID: AN00187860
• DOI: 10.2320/jinstmet1952.63.2_259
• ISSN: 18806880
• ISSN: 24337501
• ISSN: 00214876
• NDL書誌ID: 4659712
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4659712
• Web Site: https://www.jstage.jst.go.jp/article/jinstmet1952/63/2/63_2_259/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可