Phase Separation in Nearly Stoichiometric NiAl
-
- Kato Masahiko
- Department of Mechanical Engineering, Graduate School of Engineering, Kogakuin University
-
- Sasano Hisaoki
- National Research Institute for Metals
-
- Suzuki Toshiyuki
- Department of Mechanical Engineering, Graduate School of Engineering, Kogakuin University
Bibliographic Information
- Other Title
-
- 化学量論組成付近のNiAlにおける相分離
Search this article
Abstract
Authors previously reported that the interdiffusion coefficients of NiAl phase are extremely small near the stoichiometric composition below 1123 K, and that it is highly possible to induce phase separation. In this study, the microstructures of Ni-50 at%Al and Ni-48 at%Al alloys annealed at 1073 K for 8 h after slow cooling from 1623 K have been investigated by electron microscopy. The banded structure, which have major axis at right angles to ⟨\bar110⟩ direction, was observed firstly in both alloys of Ni-50 at%Al and Ni-48 at%Al near the stoichiometry. The banded structure implies the structural change in the plane parallel to the {110}. This suggests occurrence of phase separation in NiAl phase.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 63 (4), 549-550, 1999
The Japan Institute of Metals and Materials
- Tweet
Details
-
- CRID
- 1390001206490752000
-
- NII Article ID
- 10002549957
-
- NII Book ID
- AN00062446
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed