Effect of Carbide and Nitride Precipitates on the Fatigue Properties of Fe-30 mass%Cr Alloys
-
- Fukuda Tadashi
- Institute for Materials Research, Tohoku University
Bibliographic Information
- Other Title
-
- Fe-30%Cr合金の疲れ特性に及ぼす炭化物および窒化物の影響
- Fe 30パーセント Cr ゴウキン ノ ツカレ トクセイ ニ オヨボス タンカブツ オヨビ チッカブツ ノ エイキョウ
Search this article
Abstract
Effects of morphology of carbide and nitride precipitates on the fatigue strength under pulsating tension of Fe-30 mass%Cr alloys containing 0.03 mass%C and 0.03 mass%N were investigated. Two kinds of heat treatments were adopted to obtain different types of morphology of grain boundary precipitates and that of precipitates within the grains.<BR>The results obtained are summarized as follows:<BR>(1) Fatigue strength of the specimens containing grain boundary carbide and nitride is lower than that of the specimens containing carbide and nitride within the grains. The difference of fatigue strength between above mentioned two different types of morphology of carbide and nitride precipitates increase with decreasing fatigue life.<BR>(2) Fatigue strength of the specimen containing continuous, flat, and plate-like grain goundary nitride is lower than that of the specimen containing discontinuous grain boundary carbide around shorter fatigue life.<BR>(3) Initiation of fatigue crack in the specimens containing grain boundary carbide and nitride precipitates is promoted by intergranular fracture of decohesion at the interfaces between the matrix and those precipitates.<BR>(4) It is recommended to choose a heat treatment condition in which the formation of large, continuous, and flat grain boundary nitride is avoided.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 63 (5), 581-584, 1999
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681467458816
-
- NII Article ID
- 10002550047
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214426
-
- NDL BIB ID
- 4735986
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed