水素吸蔵合金の微紛化に及ぼす材料因子

DOI Web Site Web Site 参考文献6件

書誌事項

タイトル別名
  • Material Factors in the Decrepitation of Hydrogen Storage Alloys
  • スイソ キュウゾウ ゴウキン ノ ビフンカ ニ オヨボス ザイリョウ インシ

この論文をさがす

抄録

Most of hydrogen storage alloys show decrepitation during hydriding-dehydriding cycles. The decrepitation assists initial activity and reaction rate. However, it causes lowering of thermal conductivity, difficulties of handling, degradation and others. In this work, the decrepitation process was examined with regard to mechanical properties and microstructure.<BR>Four types of alloys; LaNi5, TiMn1.5, TiFe0.8C0.1 and ZrNi are used for this work. Compression test, Vickers hardness measurement and high-resolution electron microscopy observation were carried out before and after hydrogenation. Ductile alloys did not show remarkable decrepitation. Brittle alloys showed typical decrepitation, in which the nano crystal grains were observed by use of high-resolution microscopy. These results emphasize that the decrepitation process is different each other’s, depending on the ductility or brittleness of the alloys.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 63 (5), 601-604, 1999

    公益社団法人 日本金属学会

参考文献 (6)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ