テルミット型反応生成粒子分散アルミニウム合金とその耐焼付き性

• 辻川 正人

  大阪府立大学工学部　工博

• 橋本 哲

  同大学院〔現　松下電器産業（株）〕

• 日野 実

  岡山県工業技術センター　工博

• 川本 信

  大阪府立大学工学部　工博

書誌事項

タイトル別名

• Parlicle Dispersion Aluminum Alloy Produced by Thermit Reaction and Its Anti-seizure Property
• テルミットガタ ハンノウ セイセイ リュウシ ブンサン アルミニウム ゴウキン

抄録

  The process of producing alumina particle dispersion Al-Si alloy slurry, and the wear properties of the product has been investigated. A thermit type reaction occurs when SiO₂ particles are added to the molten aluminum alloy. Consequently, hard alumina particles are distributed in the matrix alloy. The content of silicon in the matrix alloy increases because of reduction of the silica by molten aluminum. The potential ability of this method was clarified by measuring the rate of particles recovery and comparing with the conventional method of adding alumina particles. The composite had as good an anti-seizure property as the alumina aluminum alloy composite made by the conventional method.

収録刊行物

• 鋳造工学

  鋳造工学 70 (2), 121-125, 1998

  公益社団法人 日本鋳造工学会

キーワード

• metal matrix composite
• Al₂O₃ particle
• thermit reaction
• wear property
• wettability

詳細情報

• CRID: 1390282681483336448
• NII論文ID: 10002553413
• NII書誌ID: AN10514770
• DOI: 10.11279/jfes.70.121
• ISSN: 21855374
• ISSN: 13420429
• NDL書誌ID: 4403062
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4403062
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可