鋳鉄へのステライトのレーザ肉盛り Laser Beam Cladding of Stellite on Cast Iron

この論文にアクセスする

この論文をさがす

著者

抄録

  CO<sub>2</sub> laser beam was applied to the cladding of stellite on cast iron by using beam scanner. The hardness and microstructure of clad layer were investigated by changing the laser power and number of clad layer. The average hardness of clad layer obtained was 480∼510 HV 0.1, when the conditions were laser power from 2200 W to 2600 W, clad number from one layer to four layers (thickness of clad layer ; 0.9∼4.7mm), cladding speed of 400mm/min, defocusing distance of 30mm, oscillated width of 7mm and argon as the shielding gas. The microstructure of clad layer was completely transformed into a fine dendritic structure (secondary dendrite arm spacing; 5.0μm) and eutectic carbide by the rapid solidification conditions. The remelted zone was produced on the surface of cast iron (base metal) and a primary dendrite and ledebulite could be observed. EPMA line analysis indicated that alloyed layer (thickness ; 150∼200 μm) existed between clad layer and base metal. These results show that CO<sub>2</sub> laser beam cladding serves as a new surface treatment process for cast iron in foundry industries.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 70(5), 323-328, 1998-05 

    Japan Foundry Engineering Society

参考文献:  18件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002553802
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    4470663
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ