生型鋳造品に発生するピンホール欠陥の走査電子顕微鏡観察 SEM Observation of Pin Hole Defects in Cast Iron by Green Sand Mold

この論文にアクセスする

この論文をさがす

著者

抄録

  This is the observation of pin hole defects occurred in cast iron by green sand mold with SEM. All 109 samples (gas hole defects) gathered from 34 foundries are observed. The defects are classified in 4 types as follows : In D), there are still more 3 types defects. A) round pin hole, B) thin & long pin hole, C) fissure pin hole, D) slag pin hole (a : ladle slag, b : inoculant, c : manganese sulfide). Typical SEM photo (A~D) is shown the figure. By standardizing these, SEM photos, it will be possible to classify the pin hole defects occurred in foundries and it will help studying of prevention.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 70(7), 495-501, 1998-07 

    Japan Foundry Engineering Society

参考文献:  13件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002554006
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    SHO
  • ISSN
    13420429
  • NDL 記事登録ID
    4516005
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ