Effects of Iron and Manganese Contents on Releasing Force of Aluminum Die Castings
-
- Nishi Naomi
- リョービ(株)研究部 工博
-
- Kami Shigetake
- RYOBI DIE CASTING (U. S. A), INC.
Bibliographic Information
- Other Title
-
- アルミニウム合金ダイカストの離型力に及ぼす鉄,マンガン量の影響
- アルミニウム ゴウキン ダイカスト ノ リケイリョク ニ オヨボス テツ マン
Search this article
Abstract
The releasing force of ADC10 die castings was measured using ejector pin type pressure sensor and the microstructure was observed in order to investigate the effect of Fe and Mn on the releasing ability. Inverse segregation with concentration of Fe, Mn and Si a two or three time higher than the average composition of Fe, Mn and Si was observed. Intermetallic compounds of Al5FeSi were observed at the surface of die casting added with 0.8 mass % Fe. Granular intermetallic compounds of Al15 (Fe, Mn)3 Si were observed at the die castings surface added with 0.8 mass % Fe and 0.4 mass % Mn. The hardness of the casting surface layer was increased by the inverse segregation of the intermetallic compounds. The releasing force of die castings without Fe and Mn increased with increasing of casting amount increased. The releasing force of the die castings which contain 0.8 mass % Fe and / or 0.4 mass % Mn did not increase.
Journal
-
- Journal of Japan Foundry Engineering Society
-
Journal of Japan Foundry Engineering Society 70 (9), 648-654, 1998
Japan Foundry Engineering Society
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681483022720
-
- NII Article ID
- 10002554185
-
- NII Book ID
- AN10514770
-
- COI
- 1:CAS:528:DyaK1cXntFaqsbw%3D
-
- ISSN
- 21855374
- 13420429
-
- NDL BIB ID
- 4564965
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
- Crossref
-
- Abstract License Flag
- Disallowed