鋳鉄鋳物に発生したスラグ入りピンホール欠陥の解析 Analysis for Slag Pinhole Defects in Cast Iron

この論文にアクセスする

この論文をさがす

著者

抄録

  It is the slag pinhole defects that is occurred frequently within gas defects. There is 3 main factors. : (a) Fe-Mn-Si slag, (b) MnS and its slag, (c) Al of inoculant and Mg of spheroidizer. (b) can be differentiated by Mn and S. (a) and (c) is difficult to be differentiated because the slag component in defects is very similar. To differentiate (a) and (c), I have tested about slag pinhole reappearance, then analyzed by SEM and EDX. In the test of using 3 different inoculant, there were a lot of C. Si and Al were also found. Mn was increased slightly. In the test of using 3 different slag, Mn and Si were found at the same place. C was increased slightly and Al was decreased. It is showed 6 examples of SEM and EDX analysis for slag pinhole defects occurred on products. To differentiate (a), (b) and (c), each element was overlapped by analyzing of EDX phase.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 71(2), 115-120, 1999-02 

    Japan Foundry Engineering Society

参考文献:  13件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002554824
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    SHO
  • ISSN
    13420429
  • NDL 記事登録ID
    4658684
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ