多合金系白鋳鉄の連続冷却変態特性 Continuous Cooling Transformation Behavior of Multi-Component White Cast Iron

この論文にアクセスする

この論文をさがす

著者

抄録

  Continuous cooling transformation behavior of Fe-5 % Cr-5 % Mo-5 % W-5 % V-2 % Co alloys with 2.0 and 2.8 % C (mass %) was investigated at two austenitizing temperatures, 1273 K and 1373 K. In spite of the difference in carbon content and austenitizing temperature, pearlite and bainite transformations were found to separate to the top and bottom individually. Regardless of the austenitizing temperature, the bainite nose was located at the short time side than the pearlite nose in low carbon cast iron. In the high carbon cast iron austenitized at 1273 K, the pearlite and bainite nose times were more or less the same, but a delay was seen in the bainite nose time in iron austenitized at 1373 K. Irrespective of the austenitizing temperature, the temperatures of pearlite and bainite noses and bainite nose time were similar in both irons. However, the time of pearlite nose in low carbon cast iron was located at the long time side compared with high carbon cast iron. The Ms temperatures appeared from 340 K to 495 K but the Mf temperatures were below room temperature. The Ms temperatures were found to be higher in the low carbon cast iron and lower in both irons austenitized at 1373 K.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 71(3), 183-189, 1999-03 

    Japan Foundry Engineering Society

参考文献:  13件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002554920
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    4683528
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ