低硫黄球状黒鉛鋳鉄のチル化及び機械的性質に及ぼすMg, REの影響 [in Japanese] Effects of Mg and RE on Mechanical Properties and Chilling of Low Sulfur Spheroidal Graphite Cast Iron [in Japanese]
Access this Article
Search this Article
The mechanical properties in thick sections and chilling in thin sections of low sulfur spheroidal graphite cast iron were investigated. Chilling could not be eliminated in thin section by Mg addition, but could be eliminated by combining Mg and RE. However, the range of the amount of RE added for eliminating chilling was extremely limited for extremely low sulfur melt. In spheroidal graphite cast iron containing Mg and RE, the high tensile strength of 500 MPa or above in thick sections (φ 30 mm) was obtained without chilling. For the extremely low sulfur cast iron, excellent elongation was obtained.
- THE JOURNAL OF THE JAPAN FOUNDRYMEN'S SOCIETY
THE JOURNAL OF THE JAPAN FOUNDRYMEN'S SOCIETY 71(4), 233-238, 1999-04
Japan Foundry Engineering Society